Polyvinyl Chloride Resin QS-1050P
Specifications
| Item | Index | |
| Appearance | White Powder | |
| Density g/cm3 | 1.4 g/mL at 25 °C(lit.) | |
| Water solubility | Less than 1 mg/mL | |
| Item | Superior quality | Qualified product | Test method | |||||
| Average polymerization degree | 1000-1100 | 1000-1100 | GB/T 5761,Appendix A | |||||
| Apparent density, g/ml | ≥0.52-0.57 | ≥0.50-0.57 | GB/T 20022 | |||||
| Volatiles content (water included), %, | ≤0.20 | ≤0.30 | GB/T2914 | |||||
| Plasticiser absorption of 100g resin%≥ | ≥ 21 | ≥ 21 | GB/T 3400 | |||||
| VCM residue, mg/kg | ≤ 3.0 | ≤ 5.0 | GB/T 4615,Appendix A | |||||
| Screenings % 250pm mesh 63pm mesh | 2.0 | 8.0 | GB/T 5761, Appendix B | |||||
| 95 | 85 | GB/T 5761, Appendix B | ||||||
| Fisheye number, No./400cm2 | 10 | 50 | GB/T 4611 | |||||
| Number of impurity particles, No | 16 | 60 | GB/T 9348 | |||||
| Whiteness (160ºC, 10 minutes later), % | 80 | 74 | GB/T 15595-95 | |||||
Packing & Storage
| Packing | A small package of this product is packed in a composite bag made of leather paper and polypropylene braid, the contents of each bag is 25 kg. The large-sized package is packed in an outer bag made of polypropylene fabric with an inner coating (PP) and an inner bag made of commercial high-pressure polyethylene (LDPE) film, the contents of each bag are 1100 kg. | |||||||
| Storage | Store in a cool, dry, and ventilated warehouse, do not stack in the open air, and do not be exposed to sunlight. In the humid and hot seasons, it should be stacked upside down once a month to facilitate moisture dissipation and ventilation. | |||||||
| Shipping | Polyvinyl Chloride is shipped in 25kg net paper-plastic bags. During transportation, clean and covered vehicles should be used to prevent rain. | |||||||
Free Quote
At present, the company has more than 10 advanced production lines of the hollow glass microspheres with the annual production capacity of 15 thousand tons. To meet the demand of customers, the company can expand production capacity as soon as possible within 20 days. 6S principles Implemented in the production systems.
For samples, pricing, or more information, please call us at 0086 25 51192301 or mail to info@ascent-chem.com or fill out the following form. We will respond to you as soon as possible.
Tel: 0086 25 51192301
E-mail: info@ascent-chem.com
General Information
| Common Names | Polyvinyl Chloride Resin QS-1050P | |||||||
| Structure |  (C2H3Cl)n |
|||||||
| CAS No. | 9002-86-2 | Boiling Point (℃) | 0.100°C | |||||
| Molecular Weight | 64.5141 | Melting Point (℃) | 85°C (185° F) | |||||
| Appearance | White Powder | Vapour Pressure | 2580mmHg at 25°C | |||||
| HS Code | 3904109001 | Flash Point (ºF) | 61.6ºC | |||||
| Solubility | Stable. Combustible. Incompatible with strong oxidizing agents. | Glass transition temperature | 87℃ | |||||
| Safety Phrases | 26-36/37-61 | ||
| RIDADR | NONH for all modes of transport | ||
| WGK Germany | 3 | ||
| Hazard Codes | Xi | ||
| Hazard Class | 2.1 | ||
| FIRST AID | |
| Inhalation | If inhaled, move the patient to fresh air. If breathing stops, perform artificial respiration. Consult a doctor. |
| Skin | If inhaled, move the patient to fresh air. If breathing stops, perform artificial respiration. Consult a doctor. |
| Eyes | Rinse thoroughly with plenty of water for at least 15 minutes and consult a doctor. |
| Ingestion | Never feed anything through the mouth to the unconscious person. Rinse your mouth with water. Consult a doctor.Consult a doctor. |
First, add distilled water (180 parts), dispersant (0.1~0.06 parts), and other additives (appropriate amount) to the polymerization kettle, purify with nitrogen and then add vinyl chloride monomer (100 parts). Stir for 15 min, heat up to 55℃, and stir continuously until. Polymerization pressure drops by 0. The reaction is stopped at 15Mpa, and the finished product is obtained after treatment.
Frequently Asked Questions
What is PVC Resin Powder ?
Polyvinyl Chloride Resin QS-1050P is a type of PVC resin used in various applications. PVC is a versatile thermoplastic polymer known for its durability, chemical resistance, and cost-effectiveness. It is widely used in construction, automotive, electrical, packaging, and other industries.
PVC resin powder refers to the powdered form of polyvinyl chloride (PVC) resin. PVC resin is a thermoplastic polymer that is synthesized from vinyl chloride monomers. It is widely used in various industries and applications due to its versatile properties.
PVC resin powder is typically produced by the polymerization of vinyl chloride monomers and subsequent processing steps. The powder form is convenient for storage, transportation, and various manufacturing processes. It is commonly used as a raw material in the production of PVC products, such as pipes, fittings, profiles, films, sheets, cables, and more.
The specific properties of PVC resin powder can vary depending on the specific grade, molecular weight, and additives used during the polymerization process. These properties can include characteristics such as hardness, flexibility, chemical resistance, and processing parameters. Different grades of PVC resin powder may be tailored for specific applications and processing methods.