Low density polyethylene resin LDPE 2102TN26
Specifications
| Item | Superior quality | Qualified product | Test method |
| Particles Color grain g/kg Large and small grains | ≤ 7 | ≤ 10 | SH/T 1541-2006 |
| ≤5 | ≤10 | ||
| Melt mass flow rate g/10min | 2.0~2.8 | 2.0~3.0 | GB/T 3682-200 |
| Density, g/cm3 | 0.919~0.922 | GB/T 1033-1986 | |
| Tensile Strength MPa | ≥ 10.0 | ≥ 9.0 | ASTM D 63803 |
| Elongation at break % | ≥ 550 | ≥ 500 | |
| Film haze % | ≤ 9.0 | ≤ 9.0 | GB/T 2410-1980 |
| Resistance to tearing (Horizontal) | ≥ 0.35 | GB/T 11999-1989 | |
| Resistance to tearingVertical | ≥ 0.45 | ||
Packing & Storage
| Packing | Packed in internally coated polypropylene woven bags, and the net content of each bag of product is 25kg | |||||||
| Storage | It should be stored in a ventilated, dry, clean, and well-maintained warehouse with good fire-fighting facilities. When storing, it should be kept away from the source of fire and prevent direct light. It is strictly forbidden to store in the open air. The storage period generally does not exceed 12 months from the date of production. | |||||||
| Shipping | Sharp tools such as iron hooks are prohibited during transportation, loading, and unloading. During transportation should be kept clean, dry, and equipped with compartments or clothes. It shall not be mixed with sand, broken metal, coal, glass, etc. during transportation. | |||||||
Free Quote
At present, the company has more than 10 advanced production lines of the hollow glass microspheres with the annual production capacity of 15 thousand tons. To meet the demand of customers, the company can expand production capacity as soon as possible within 20 days. 6S principles Implemented in the production systems.
For samples, pricing, or more information, please call us at 0086 25 51192301 or mail to info@ascent-chem.com or fill out the following form. We will respond to you as soon as possible.
Tel: 0086 25 51192301
E-mail: info@ascent-chem.com
General Information
| Common Names | Low Density Polyethylene 2102TN00，LDPE 2102TN00 | |||||||
| Structure |  (C2H4)n |
|||||||
| CAS No. | 9002-88-4 | Boiling Point (℃) | 48-110 °C(Press: 9 Torr) | |||||
| Molecular Weight | 28.05316 | Melting Point (℃) | 131 ℃ | |||||
| Appearance | White Powder | EINECS | 618-339-3 | |||||
| HS Code | 39012000 | Flash Point (ºF) | 270 °C | |||||
| Solubility | Soluble in acetone and benzene | LogP | 1.02620 | |||||
| Safety Phrases | 22-24/25 | ||
| RIDADR | NONH for all modes of transport | ||
| WGK Germany | 3 | ||
| Hazard Codes | Xi | ||
| Hazard Class | 2.1 | ||
| FIRST AID | |
| Inhalation | If inhaled, move the patient to fresh air. If breathing stops, perform artificial respiration. Consult a doctor. |
| Skin | If inhaled, move the patient to fresh air. If breathing stops, perform artificial respiration. Consult a doctor. |
| Eyes | Rinse thoroughly with plenty of water for at least 15 minutes and consult a doctor. |
| Ingestion | Never feed anything through the mouth to the unconscious person. Rinse your mouth with water. Consult a doctor.Consult a doctor. |
According to the polymerization method, low-density polyethylene can be divided into the high-pressure method and low-pressure method. According to the type of reactor, it can be divided into the kettle method and the tube method. Using ethylene as raw material, it is fed into the reactor, and the polymerization reaction is carried out by high-pressure compression under the action of the initiator. The material coming out of the reactor, after the unreacted ethylene is removed by the separator, it is melted, extruded, granulated, dried, blended, and sent for packaging.
Frequently Asked Questions
Application of LDPE 2102TN26
Low-density polyethylene resin LDPE 2102TN26 is a type of LDPE commonly used in various applications. LDPE is a thermoplastic polymer known for its flexibility, toughness, and chemical resistance. LDPE 2102TN26 refers to a grade of LDPE resin produced by a specific manufacturer or supplier.
LDPE 2102TN26 has several potential uses, including:
1. Film and Packaging: LDPE is widely used to produce thin films and flexible packaging materials. It can be used for plastic bags, shrink wrap, stretch film, agricultural films, and disposable food containers. The LDPE 2102TN26 grade may offer properties suitable for certain film applications, such as good clarity or tear resistance.
2. Coatings: LDPE can be formulated into coatings or adhesives for various purposes. It can provide protection and moisture resistance or improve the surface properties of materials. LDPE 2102TN26 might be used in paper, textiles, or other substrates coatings.
3. Wire and Cable Insulation: LDPE can be an insulation material for electrical wires and cables. Its electrical properties, flexibility, and moisture resistance suit this application. LDPE 2102TN26 may have specific characteristics optimized for wire and cable insulation.
4. Molded Parts: LDPE can be molded into various shapes and forms, such as containers, lids, caps, toys, and automotive parts. The LDPE 2102TN26 grade might be formulated to provide specific properties, such as improved impact resistance or dimensional stability.
It’s important to note that the specific application and performance requirements will dictate the suitability of LDPE 2102TN26. Manufacturers or suppliers typically provide technical data sheets and guidance on their specific LDPE grades’ recommended uses and processing conditions.