Low density polyethylene resin 2102TN00
Specifications
| Item | Superior quality | Qualified product | Test method |
| Particles Color grain g/kg Large and small grains | ≤ 7 | ≤ 10 | SH/T 1541-2006 |
| ≤5 | ≤10 | ||
| Melt mass flow rate g/10min | 2.0~2.8 | 1.8~3.0 | GB/T 3682-200 |
| Density, g/cm3 | 0.919~0.922 | GB/T 1033-1986 | |
| Tensile Strength MPa | ≥ 10.0 | ≥ 9.0 | ASTM D 63803 |
| Elongation at break % | ≥ 550 | ≥ 500 | |
| Film haze % | ≤ 9.0 | ≤ 9.0 | GB/T 2410-1980 |
| Resistance to tearing (Horizontal) | ≥ 0.35 | GB/T 11999-1989 | |
| Resistance to tearingVertical | ≥ 0.45 | ||
Packing & Storage
| Packing | Packed in internally coated polypropylene woven bags, and the net content of each bag of product is 25kg | |||||||
| Storage | It shall not be mixed with sand, broken metal, coal, glass, etc. during transportation. Exposure to sunlight or rain is strictly prohibited. It should be stored in a ventilated, dry, clean, and well-maintained warehouse with good fire-fighting facilities. When storing, it should be kept away from the source of fire and prevent direct light. It is strictly forbidden to store in the open air. The storage period generally does not exceed 12 months from the date of production. | |||||||
| Shipping | Sharp tools such as iron hooks are prohibited during transportation, loading, and unloading. During transportation should be kept clean, dry, and equipped with compartments or clothes. It shall not be mixed with sand, broken metal, coal, glass, etc. during transportation. | |||||||
Free Quote
At present, the company has more than 10 advanced production lines of the hollow glass microspheres with the annual production capacity of 15 thousand tons. To meet the demand of customers, the company can expand production capacity as soon as possible within 20 days. 6S principles Implemented in the production systems.
For samples, pricing, or more information, please call us at 0086 25 51192301 or mail to info@ascent-chem.com or fill out the following form. We will respond to you as soon as possible.
Tel: 0086 25 51192301
E-mail: info@ascent-chem.com
General Information
| Common Names | Low Density Polyethylene 2102TN00，LDPE 2102TN00 | |||||||
| Structure |  (C2H4)n |
|||||||
| CAS No. | 9002-88-4 | Boiling Point (℃) | 48-110 °C(Press: 9 Torr) | |||||
| Molecular Weight | 28.05316 | Melting Point (℃) | 131 ℃ | |||||
| Appearance | White Powder | EINECS | 618-339-3 | |||||
| HS Code | 39012000 | Flash Point (ºF) | 270 °C | |||||
| Solubility | Soluble in acetone and benzene | LogP | 1.02620 | |||||
| Safety Phrases | 22-24/25 | ||
| RIDADR | NONH for all modes of transport | ||
| WGK Germany | 3 | ||
| Hazard Codes | Xi | ||
| Hazard Class | 2.1 | ||
| FIRST AID | |
| Inhalation | If inhaled, move the patient to fresh air. If breathing stops, perform artificial respiration. Consult a doctor. |
| Skin | If inhaled, move the patient to fresh air. If breathing stops, perform artificial respiration. Consult a doctor. |
| Eyes | Rinse thoroughly with plenty of water for at least 15 minutes and consult a doctor. |
| Ingestion | Never feed anything through the mouth to the unconscious person. Rinse your mouth with water. Consult a doctor.Consult a doctor. |
According to the polymerization method, low-density polyethylene can be divided into the high-pressure method and low-pressure method. According to the type of reactor, it can be divided into the kettle method and the tube method. Using ethylene as raw material, it is fed into the reactor, and the polymerization reaction is carried out by high-pressure compression under the action of the initiator. The material coming out of the reactor, after the unreacted ethylene is removed by the separator, it is melted, extruded, granulated, dried, blended, and sent for packaging.
Frequently Asked Questions
LDPE 2102TN00 Resin Overview
Low-density polyethylene (LDPE) resin 2102TN00 is a specific grade of LDPE that is commonly used in various applications. LDPE is a type of thermoplastic made from the monomer ethylene, and it is known for its flexibility, toughness, and low melting point.
LDPE resin 2102TN00 is typically used in film and packaging applications where a combination of strength and flexibility is required. It offers good processability, excellent impact resistance, and low-temperature properties. The “2102TN00” designation is a specific product code or grade given by the resin manufacturer to identify this particular formulation.
LDPE resin 2102TN00 may be used in the production of plastic bags, agricultural films, shrink films, and various types of packaging materials. It can also be blended with other polymers or additives to modify its properties based on specific application requirements.
It’s worth noting that while LDPE is widely used, it is not suitable for all applications. Its low density and relatively low strength make it less suitable for applications that require high rigidity or structural integrity. In such cases, other types of plastics, such as high-density polyethylene (HDPE) or polypropylene (PP), may be more suitable.